Crucible PDCQ Premium Quality High Toughness H13 |
||||||||||||||||||||||||||||||||||||||||||||||
Crucible PDCQ is a premium version of H13, manufactured to exceed die casting industry specifications. PDCQ has at least 10 ft. lbs room temerature transverse toughness. Its enhanced toughness promotes die life and minimizes failures due to cracking. Remelted and specially refined, PDCQ is an extremely clean steel which can be polished to a critical finish for injection molds. PDCQ is tested by an independent metallurgical laboratory for certification of the microstructural quality rating and toughness measurements. |
||||||||||||||||||||||||||||||||||||||||||||||
|
|
|||||||||||||||||||||||||||||||||||||||||||||
|
||||||||||||||||||||||||||||||||||||||||||||||
|
||||||||||||||||||||||||||||||||||||||||||||||
Annealing Either of the following two procedures is acceptable: A. Heat to 1600°F, hold 2 hrs. at temperature. Cool slowly (25°F/hr. maximum cooling rate) to 1200°F, then air cool to room temperature. B. Heat to 1600°F, hold 2 hrs. at temperature. Cool to 1400°F, hold 6 hrs. at temperature, then air cool to room temperature. Typical Annealed Hardness: BHN 192/235 Stress Relieving Annealed Material: Heat uniformly to 1200/1250°F, hold 2 hrs. at temperature. Cool in still air to room temperature. Hardened Material: Heat uniformly to 25/50°F below tempering temperature, hold 2 hrs. Cool in still air to room temperature. Dimensional Changes on Heat Treating The average dimensional change for normally heat treated PDQC is the same as for Nu-Die XL. Surface Treatments PDCQ is suitable for the same surface treatments as Nu-Die XL. Welding PDCQ can be successfully welded using the same techniques and filler metals that are used for Nu-Die XL. Physical Properties Modulus of Elasticity ...........................................................30 psi x 106 Density ..................................................................................0.280 lbs/in3 Thermal Conductivity .........................................200°.......................................15 BTU/hr/ft/°F .........................................600°F ...................................16 BTU/hr/ft/°F Thermal Expansion RT 200°F .............................................................6.1 x 10-6 in/in/°F 200° 400°F ...........................................................6.4 x 10-6 in/in/°F 400° 800°F ...........................................................6.8 x 10-6 in/in/°F 800° 1000°F ........................................................7.0 x 10-6 in/in/°F 1000° 1200°F ......................................................7.3 x 10-6 in/in/°F |
||||||||||||||||||||||||||||||||||||||||||||||
|